Corrosion Resistance of Some Amorphous Metallic Fe–P–M (M = Si, Nb, Mo) Alloys: Effects of Composition, Structural Relaxation, Partial Crystallization, and Local Deformation
- Авторлар: Ievlev V.1,2, Il’inova T.2, Kannykin S.2, Bobrinskaya E.2, Vavilova V.3, Serikov D.4, Kushchev S.4
-
Мекемелер:
- Moscow State University
- Voronezh State University
- Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences
- Voronezh State Technical University
- Шығарылым: Том 2019, № 3 (2019)
- Беттер: 210-215
- Бөлім: Article
- URL: https://journals.rcsi.science/0036-0295/article/view/173100
- DOI: https://doi.org/10.1134/S0036029519030054
- ID: 173100
Дәйексөз келтіру
Аннотация
The corrosion resistance of metallic amorphous alloys (AAs) Fe80.2P17.1Mo2.7, Fe80.5P18.4Nb1.1, Fe98 –xPxSi2 (x = 14, 16, 20), Fe76.5P13.6Si4.8Mn2.4V0.2C2.5 in a 0.1 M solution of Na2SO4 (pH 6.25) and its change due to structural relaxation, nanocrystallization, and local deformation are studied. The activation of structural relaxation by photonic treatment is shown to increase the corrosion resistance of AAs. As the phosphorus content in the Fe98 ‒ xPxSi2 system decreases, the corrosion resistance of AAs decreases because of partial crystallization, which is accompanied by the formation of iron phosphides during rapid cooling of a melt, and silicon segregation at phase boundaries. The formation of local deformation zones in the near-surface layer of Fe76.5P13.6Si4.8Mn2.4V0.2C2.5 AA decreases its corrosion resistance. The niobium alloying of Fe‒P AAs is shown to be effective to decrease the corrosion rate.
Авторлар туралы
V. Ievlev
Moscow State University; Voronezh State University
Email: svkannykin@gmail.com
Ресей, Moscow, 119991; Voronezh, 394036
T. Il’inova
Voronezh State University
Email: svkannykin@gmail.com
Ресей, Voronezh, 394036
S. Kannykin
Voronezh State University
Хат алмасуға жауапты Автор.
Email: svkannykin@gmail.com
Ресей, Voronezh, 394036
E. Bobrinskaya
Voronezh State University
Email: svkannykin@gmail.com
Ресей, Voronezh, 394036
V. Vavilova
Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences
Email: svkannykin@gmail.com
Ресей, Moscow, 119991
D. Serikov
Voronezh State Technical University
Email: svkannykin@gmail.com
Ресей, Voronezh, 394000
S. Kushchev
Voronezh State Technical University
Email: svkannykin@gmail.com
Ресей, Voronezh, 394000
![](/img/style/loading.gif)