Possibility to Strengthen the Joint between a Titanium Alloy and Stainless Steel Formed by Diffusion Welding through an Interlayer
- Авторлар: Khazgaliev R.1, Imayev M.1,2, Mulyukov R.1,2
-
Мекемелер:
- Institute for Metals Superplasticity Problems
- Bashkir State University
- Шығарылым: Том 2018, № 4 (2018)
- Беттер: 341-347
- Бөлім: Advanced Materials and Technologies
- URL: https://journals.rcsi.science/0036-0295/article/view/172466
- DOI: https://doi.org/10.1134/S0036029518040067
- ID: 172466
Дәйексөз келтіру
Аннотация
The mechanical properties and the fracture of the joints between a PT3V titanium alloy and 12Cr18Ni10Ti stainless steel formed by diffusion welding through ultrafine-grained layers of nickel and a Cr2Ni98 alloy are studied. The highest strength of the joint (about 390 MPa) is achieved upon welding at T = 700°C, 20 min irrespective of the interlayer material. However, in the case of the nickel interlayer, fracture occurs in the regions adjacent to the TiNi layer; in the case of the Cr2Ni98 alloy, along the alloy/steel interface.
Негізгі сөздер
Авторлар туралы
R. Khazgaliev
Institute for Metals Superplasticity Problems
Хат алмасуға жауапты Автор.
Email: sloth-usatu@mail.ru
Ресей, Ufa, 450001
M. Imayev
Institute for Metals Superplasticity Problems; Bashkir State University
Email: sloth-usatu@mail.ru
Ресей, Ufa, 450001; Ufa, 450076
R. Mulyukov
Institute for Metals Superplasticity Problems; Bashkir State University
Email: sloth-usatu@mail.ru
Ресей, Ufa, 450001; Ufa, 450076
![](/img/style/loading.gif)