Мақаланы E-mail арқылы жіберу Iron–Chromium Precursors for Hard-Magnetic Fe–Cr–Co Alloys
- Авторлар: Vedmid L.1,2, Dorogina G.1
-
Мекемелер:
- Institute of Metallurgy, Ural Branch
- El’tsin Ural Federal University
- Шығарылым: Том 2018, № 2 (2018)
- Беттер: 114-117
- Бөлім: Article
- URL: https://journals.rcsi.science/0036-0295/article/view/172243
- DOI: https://doi.org/10.1134/S0036029518020222
- ID: 172243
Дәйексөз келтіру
Ашық рұқсат
Рұқсат берілді
Тек жазылушылар үшін
Аннотация
The effect of the chromium concentration on the magnetic properties of Fe–Cr precursors for hard-magnetic Fe–Cr–Co materials is studied. Nitrogen used as a sintering atmosphere and a long annealing time enhance are found to increase the coercive force Hc of the materials. The phase formation in Fe–30% Cr alloys is traced during heat treatment in nitrogen and argon atmosphere using thermal analysis.
Негізгі сөздер
Авторлар туралы
L. Vedmid
Institute of Metallurgy, Ural Branch; El’tsin Ural Federal University
Хат алмасуға жауапты Автор.
Email: elarisa100@mail.ru
Ресей, Yekaterinburg, 620016; Yekaterinburg, 620002
G. Dorogina
Institute of Metallurgy, Ural Branch
Email: elarisa100@mail.ru
Ресей, Yekaterinburg, 620016