Effect of corrosive media on the cracking resistance of pipe steel under load
- Авторлар: Musaev S.1, Betsofen S.1
-
Мекемелер:
- Moscow Aviation Institute (National Research University)
- Шығарылым: Том 2016, № 10 (2016)
- Беттер: 981-985
- Бөлім: Applied Problems of Strength and Plasticity
- URL: https://journals.rcsi.science/0036-0295/article/view/170956
- DOI: https://doi.org/10.1134/S0036029516100141
- ID: 170956
Дәйексөз келтіру
Аннотация
The kinetics of fatigue crack propagation has been studied in full-thickness specimens cut from a main pipeline under the simultaneous action of a cyclic load and a hydrogen sulfide-containing corrosive medium. The degradation mechanisms of the material are discussed using the results of optical microscopy.
Негізгі сөздер
Авторлар туралы
S. Musaev
Moscow Aviation Institute (National Research University)
Email: s.betsofen@gmail.ru
Ресей, Volokolamskoe sh. 4, Moscow, 121552
S. Betsofen
Moscow Aviation Institute (National Research University)
Хат алмасуға жауапты Автор.
Email: s.betsofen@gmail.ru
Ресей, Volokolamskoe sh. 4, Moscow, 121552