Gas release from an E125 zirconium alloy under hydrogenation and deformation conditions
- Авторлар: Tyurin Y.1, Larionov V.1, Nikitenkov N.1
-
Мекемелер:
- National Research Tomsk Polytechnic University
- Шығарылым: Том 2016, № 9 (2016)
- Беттер: 875-878
- Бөлім: Article
- URL: https://journals.rcsi.science/0036-0295/article/view/170885
- DOI: https://doi.org/10.1134/S0036029516090159
- ID: 170885
Дәйексөз келтіру
Аннотация
The degassing from a hydrogen-saturated E125 zirconium alloy is studied as a function of its deformation. Zirconium alloy samples are subjected to tension at a relative elongation of 2.5, 5, and 10%. Undeformed and deformed samples were saturated with hydrogen by a galvanic method at a current density of 0.5 A/cm2; that is, they are hydrogen saturated and then deformed. As a result, the defects at which hydrogen is trapped in zirconium are identified. The quantity of hydrogen trapped by defects depends on the strain and the sequence of deformation and hydrogen saturation. This is a technical result of the investigations, which can be used to find optimum operation conditions for hydrogen-saturated zirconium articles.
Авторлар туралы
Yu. Tyurin
National Research Tomsk Polytechnic University
Хат алмасуға жауапты Автор.
Email: tyurin@tpu.ru
Ресей, pr. Lenina 30, Tomsk, 634050
V. Larionov
National Research Tomsk Polytechnic University
Email: tyurin@tpu.ru
Ресей, pr. Lenina 30, Tomsk, 634050
N. Nikitenkov
National Research Tomsk Polytechnic University
Email: tyurin@tpu.ru
Ресей, pr. Lenina 30, Tomsk, 634050