Fracture mechanism of a thermal barrier coating
- Авторлар: Samoilenko V.1, Ravilov R.2, Drevnyak V.1, Petrova M.1
-
Мекемелер:
- Moscow State Technical University of Civil Aviation
- Lytkarino Machine-Building Plant
- Шығарылым: Том 2016, № 6 (2016)
- Беттер: 555-558
- Бөлім: Hardening and Coating Technologies
- URL: https://journals.rcsi.science/0036-0295/article/view/170624
- DOI: https://doi.org/10.1134/S0036029516060124
- ID: 170624
Дәйексөз келтіру
Аннотация
The fracture mechanism of the thermal barrier coating of gas turbine blades is studied. The causes of the fracture of the ceramic layer are discussed and the possible ways to increase the fatigue life of the thermal barrier coating are considered.
Авторлар туралы
V. Samoilenko
Moscow State Technical University of Civil Aviation
Хат алмасуға жауапты Автор.
Email: v-sam61@mail.ru
Ресей, Moscow, 125993
R. Ravilov
Lytkarino Machine-Building Plant
Email: v-sam61@mail.ru
Ресей, Lytkarino, Moscow obl., 140080
V. Drevnyak
Moscow State Technical University of Civil Aviation
Email: v-sam61@mail.ru
Ресей, Moscow, 125993
M. Petrova
Moscow State Technical University of Civil Aviation
Email: v-sam61@mail.ru
Ресей, Moscow, 125993