Long-Term Annealing Resistance of Ferritic Chromium Steels Subjected to High-Temperature Nitriding
- 作者: Nikulin S.1, Khatkevich V.1, Rogachev S.1, Bekkaliev B.1, Belov V.1
-
隶属关系:
- National University of Science and Technology MISiS
- 期: 卷 2019, 编号 4 (2019)
- 页面: 427-430
- 栏目: Applied Problems of Strength and Plasticity
- URL: https://journals.rcsi.science/0036-0295/article/view/173200
- DOI: https://doi.org/10.1134/S0036029519040268
- ID: 173200
如何引用文章
详细
The influence of long-term annealing (at 700°C, 30 h) on the structure and mechanical properties of ferritic chromium steels 08Kh17T and 15Kh25T has been comparatively studied after high-temperature nitriding and heat treatment (annealing). Both steels in all considered states are characterized by high resistance against oxidation during long-term annealing. Long-term annealing of the steels in the initial non-nitrided state and after nitriding and intermediate annealing at 700°C leads to a decrease in the ultimate tensile strength and yield strength by 10–15%. The maximum decrease in the strength (by 1.2–1.7 times) upon long-term annealing is observed in both steels after preliminary nitriding and annealing at 550°C due to partial coagulation of the nitride phase.
作者简介
S. Nikulin
National University of Science and Technology MISiS
Email: csaap@mail.ru
俄罗斯联邦, Moscow, 119049
V. Khatkevich
National University of Science and Technology MISiS
Email: csaap@mail.ru
俄罗斯联邦, Moscow, 119049
S. Rogachev
National University of Science and Technology MISiS
编辑信件的主要联系方式.
Email: csaap@mail.ru
俄罗斯联邦, Moscow, 119049
B. Bekkaliev
National University of Science and Technology MISiS
Email: csaap@mail.ru
俄罗斯联邦, Moscow, 119049
V. Belov
National University of Science and Technology MISiS
Email: csaap@mail.ru
俄罗斯联邦, Moscow, 119049
![](/img/style/loading.gif)