Structure and Tribological Properties of B83 Babbit–Based Composite Rods and the Coatings Produced from Them by Arc Surfacing

Abstract

Surfacing composite rods based on a B83 babbit alloy reinforced by silicon carbide and boron carbide particles are fabricated by extrusion. The structure and the tribological properties of the rods are studied. Extrusion allowed us to introduce and to uniformly distribute reinforcing fillers and to change the size and the morphology of the intermetallic phases in the matrix alloy. The wear resistance of the rods made of the B83 babbit + 5 wt % SiC composite material is shown to be higher than that of commercial B83 alloy samples by a factor of 1.2. Arc surfacing is used to deposit antifriction coatings, which are made of the surfacing composite rods based on B83 babbit reinforced by boron carbide or silicon carbide particles, onto steel substrates. The deposited layers exhibit good adhesion to the substrates: the melting line is continuous and does not contain discontinuities. The structure and the tribological properties of the deposited coatings are studied. The wear resistance of the composite coatings is higher than that of the B83 alloy–based coating by 30%.