Corrosion-electrochemical behavior of zirconium in molten alkali metal carbonates

Abstract

The corrosion and electrochemical characteristics of zirconium during its interaction with molten lithium, sodium, and potassium carbonates containing from 1 to 5 wt % additives to the salt phase are studied in a temperature range of 500–800°C using gravimetry, corrosion potential measurement, and anodic polarization. The substances decreasing the corrosion losses due to the strengthening and thickening of an oxide film (lithium, sodium, potassium hydroxides) are used as passivators. Sodium chloride, fluoride, and sulfate serve as corrosion stimulators (activators).