Enviar artigo por via de e-mail Effect of the cooling rate on the phase composition of crystallized CdGeAs2 melts
- Autores: Aronov A.N.1, Marenkin S.F.1,2, Fedorchenko I.V.1
-
Afiliações:
- Kurnakov Institute of General and Inorganic Chemistry
- National University of Science and Technology “Moscow Institute of Steel and Alloys”
- Edição: Volume 62, Nº 12 (2017)
- Páginas: 1645-1651
- Seção: Physicochemical Analysis of Inorganic Systems
- URL: https://journals.rcsi.science/0036-0236/article/view/168255
- DOI: https://doi.org/10.1134/S003602361712004X
- ID: 168255
Citar
Acesso aberto
Acesso está concedido
Somente assinantes
Resumo
The formation of metastable Cd3Ge2As4 was established using a set of physicochemical analysis methods. The annealing of this compound at temperatures ≥450°C was shown to lead to the formation of the stable binary eutectic Cd3As2–СdGeAs2 and ternary eutectic Cd3As2–СdGeAs2–CdAs2 with the following composition (at %): Cd, 42.20; Ge, 15.69; As, 42.11; and Cd, 42.70; Ge, 15.06; As, 42.24, respectively.
Sobre autores
A. Aronov
Kurnakov Institute of General and Inorganic Chemistry
Email: marenkin@rambler.ru
Rússia, Moscow, 119991
S. Marenkin
Kurnakov Institute of General and Inorganic Chemistry; National University of Science and Technology “Moscow Institute of Steel and Alloys”
Autor responsável pela correspondência
Email: marenkin@rambler.ru
Rússia, Moscow, 119991; Moscow, 119991
I. Fedorchenko
Kurnakov Institute of General and Inorganic Chemistry
Email: marenkin@rambler.ru
Rússia, Moscow, 119991
Arquivos suplementares