Enviar artigo por via de e-mail Hydrothermal synthesis and microstructure of α-Zn2SiO4:V crystal phosphor
- Autores: Zaitseva N.A.1, Krasnenko T.I.1, Onufrieva T.A.1, Samigullina R.F.1
-
Afiliações:
- Institute of Solid State Chemistry, Ural Branch
- Edição: Volume 62, Nº 2 (2017)
- Páginas: 168-171
- Seção: Synthesis and Properties of Inorganic Compounds
- URL: https://journals.rcsi.science/0036-0236/article/view/167363
- DOI: https://doi.org/10.1134/S0036023617020218
- ID: 167363
Citar
Acesso aberto
Acesso está concedido
Somente assinantes
Resumo
A morphologically uniform single-phase crystal phosphor α-Zn2SiO4:V was prepared by one-pot hydrothermal synthesis. Energy dispersive analysis showed that a zinc silicate-base solid solution was formed with a vanadium content of 10 ± 1 at %. Its luminescence spectrum was a broad luminescence band in the region 400–700 nm with a peak near 540 nm.
Sobre autores
N. Zaitseva
Institute of Solid State Chemistry, Ural Branch
Autor responsável pela correspondência
Email: natalzay@yandex.ru
Rússia, ul. Pervomaiskaya 91, Yekaterinburg, 620990
T. Krasnenko
Institute of Solid State Chemistry, Ural Branch
Email: natalzay@yandex.ru
Rússia, ul. Pervomaiskaya 91, Yekaterinburg, 620990
T. Onufrieva
Institute of Solid State Chemistry, Ural Branch
Email: natalzay@yandex.ru
Rússia, ul. Pervomaiskaya 91, Yekaterinburg, 620990
R. Samigullina
Institute of Solid State Chemistry, Ural Branch
Email: natalzay@yandex.ru
Rússia, ul. Pervomaiskaya 91, Yekaterinburg, 620990
Arquivos suplementares