Synthesis, structure formation, and thermal expansion of A+M2+MgE4+(PO4)3

Аннотация

The compounds AMMgE(PO₄)₃ (A = Na, K, Rb, Cs; M = Sr, Pb, Ba; E = Ti, Zr) were synthesized by the sol–gel procedure followed by heat treatment and studied by X-ray diffraction, differential thermal and electron microprobe analysis, and IR spectroscopy. The phosphates crystallize in the kosnarite (KZr₂(PO₄)₃, space group \(R\bar 3\)) and langbeinite (K₂Mg₂(SO₄)₃, space group P2₁3) structural types. The structure of KPbMgTi(PO₄)₃ was refined by full-profile analysis (space group P2₁3, Z = 4, a = 9.8540(3) Å, V = 956.83(4) ų). The structure is formed by a framework of vertex-sharing MgO₆ and TiO₆ octahedra and PO₄ tetrahedra. The K and Pb atoms fully occupy the extra-framework cavities and are coordinated to nine oxygen atoms. A variable-temperature X-ray diffraction study of KPbMgTi(PO₄)₃ showed that the compound expands isotropically and refer to medium-expansion class (linear thermal expansion coefficients α_a = α_b = α_c = 8 × 10^–6°C^–1). The number of stretching and bending modes of the PO₄ tetrahedron observed in the IR spectra is in agreement with that predicted by the factor group analysis of vibrations for space groups \(R\bar 3\) and P2₁3. A structural transition from the cubic langbeinite to the rhombohedral kosnarite was found for CsSrMgZr(PO₄)₃. In the morphotropic series of ASrMgZr(PO₄)₃ (A = Na, K, Rb, Cs) the kosnarite–langbeinite transition occurs upon the Na → K replacement. The effect of the sizes and electronegativities of cations combined in AMMgE(PO₄)₃ on the change of the structural type was analyzed.