电邮这篇文章 Т–х Diagram of Section BiB3O6–YbBO3
- 作者: Asadov M.M.1, Akhmedova N.A.1
-
隶属关系:
- Institute of Catalysis and Inorganic Chemistry of the National Academy of Sciences of Azerbaijan
- 期: 卷 63, 编号 12 (2018)
- 页面: 1617-1621
- 栏目: Physicochemical Analysis of Inorganic Systems
- URL: https://journals.rcsi.science/0036-0236/article/view/169152
- DOI: https://doi.org/10.1134/S0036023618120021
- ID: 169152
如何引用文章
开放存取
##reader.subscriptionAccessGranted##
订阅存取
详细
Phase equilibria were studied and a Т–х diagram of section BiB3O6–YbBO3 was constructed using X-ray powder diffraction and differential thermal analysis (DTA). The diagram has a peritectic point lying near 95 mol % BiB3O6 at 810°С. A limited subsolidus solubility of the components is observed in α-BiB3O6 in the range 0 ≤ х ≤ 0.3 YbBO3.
作者简介
M. Asadov
Institute of Catalysis and Inorganic Chemistry of the National Academy of Sciences of Azerbaijan
编辑信件的主要联系方式.
Email: mirasadov@gmail.com
阿塞拜疆, Baku, 1143
N. Akhmedova
Institute of Catalysis and Inorganic Chemistry of the National Academy of Sciences of Azerbaijan
Email: mirasadov@gmail.com
阿塞拜疆, Baku, 1143
补充文件