New Phosphate-Sulfates with NZP Structure

Abstract

NaZr_2–xB_x(PO₄)_3–2x(SO₄)_2x (0 ≤ x ≤ 1.25, B = Mg, Co, Ni, Cu, Zn), and NaZr_2–xR_x(PO₄)_3–x(SO₄)_x (0 ≤ x ≤ 1.25, R = Al, Fe) phosphate-sulfates series have been prepared by a sol–gel process. These compounds belong to the NaZr₂(PO₄)₃ (NZP) structure family and crystallize in hexagonal crystal system, space group R\(\bar 3\)c. Limited solid solution series were found to exist; their formation temperatures and thermal stability limits were determined. Particle sizes as determined by microstructure observation were 50–200 nm, and for Cu- and Zn-containing samples, 200–500 nm. The thermal expansion of phosphate-sulfate NaZr_1.25Cu_0.75(PO₄)_1.5(SO₄)_1.5 was studied in the range 25–700°C. Thermal expansion coefficients and thermal expansion anisotropy were found to be α_a =–5.40 × 10^–6 °C^–1, α_с = 18.88 × 10^–6 °C^–1, α_avg = 2.69 × 10^–6 °C^–1, and Δα = 24.28 × 10^–6 °C^–1.