Отправить статью по E-mail Microstructure Homogeneity and Mechanical Properties of Large-Size As-Cast High Nb Containing TiAl Alloy Ingot
- Авторы: Xu M.1,2, Zhang C.J.1,2, Han J.C.3, Chen Y.F.4, Kong F.T.5, Chen Y.Y.5, Zhang S.Z.1,2
-
Учреждения:
- School of Materials Science and Engineering, Taiyuan University of Technology
- Shanxi Key Laboratory of Advanced Magnesium-based Materials, Taiyuan University of Technology
- School of Mechanical Engineering, Taiyuan University of Technology
- Ningbo Branch of China Ordnance Academy
- National Key Laboratory for Precision Hot Processing of Metals, Harbin Institute of Technology
- Выпуск: Том 119, № 9 (2018)
- Страницы: 899-906
- Раздел: Strength and Plasticity
- URL: https://journals.rcsi.science/0031-918X/article/view/167832
- DOI: https://doi.org/10.1134/S0031918X1809017X
- ID: 167832
Цитировать
Открытый доступ
Доступ предоставлен
Только для подписчиков
Аннотация
The high Nb containing TiAl alloy with a nominal composition of Ti–44Al–8Nb–0.2W–0.2B–0.1Y was fabricated by a Vacuum Arc Remelting furnace. The microstructure and mechanical properties of specimens located in different sites of the ingot were investigated. Owing to the influence of melting process and electrode fabricating method, the morphologies and phase containing of this near lamellar structure in the top, middle, and bottom parts of ingot were different. The subtle difference in microstructure strongly influenced the room and high-temperature tensile properties in turn. However, the dominant influence factor of the mechanical properties was the defects at the bottom of this large-size ingot, though the bottom had the finest grain size.
Ключевые слова
Об авторах
M. Xu
School of Materials Science and Engineering, Taiyuan University of Technology; Shanxi Key Laboratory of Advanced Magnesium-based Materials, Taiyuan University of Technology
Email: hanjianchao@tyut.edu
Китай, Taiyuan, 030024; Taiyuan, 030024
C. Zhang
School of Materials Science and Engineering, Taiyuan University of Technology; Shanxi Key Laboratory of Advanced Magnesium-based Materials, Taiyuan University of Technology
Email: hanjianchao@tyut.edu
Китай, Taiyuan, 030024; Taiyuan, 030024
J. Han
School of Mechanical Engineering, Taiyuan University of Technology
Автор, ответственный за переписку.
Email: hanjianchao@tyut.edu
Китай, Taiyuan, 030024
Y. Chen
Ningbo Branch of China Ordnance Academy
Email: hanjianchao@tyut.edu
Китай, Ningbo, 315000
F. Kong
National Key Laboratory for Precision Hot Processing of Metals, Harbin Institute of Technology
Email: hanjianchao@tyut.edu
Китай, Harbin, 150001
Y. Chen
National Key Laboratory for Precision Hot Processing of Metals, Harbin Institute of Technology
Email: hanjianchao@tyut.edu
Китай, Harbin, 150001
S. Zhang
School of Materials Science and Engineering, Taiyuan University of Technology; Shanxi Key Laboratory of Advanced Magnesium-based Materials, Taiyuan University of Technology
Автор, ответственный за переписку.
Email: zhshzh1984@163.com
Китай, Taiyuan, 030024; Taiyuan, 030024
Дополнительные файлы