Effects of Different Quenching Treatments on Thermal Properties and Microstructure in Quaternary Cu-Based HTSMA


Citar

Texto integral

Acesso aberto Acesso aberto
Acesso é fechado Acesso está concedido
Acesso é fechado Somente assinantes

Resumo

In this study, some physical properties of a quaternary Cu-based alloy have been studied on the example of the alloy Cu–13Al–4.5Ni–1.5Ti (wt %) that was produced by using the arc-melting method. Four specimens were made from the alloy ingot, and three of them were subjected to heat treatment at 930°C for 30 min. Later, they were separately quenched into liquid nitrogen (–196°C), alcohol (0°C), and iced-brine (6°C) mediums. Differential Scanning Calorimetry (DSC) measurements of all samples were performed to determine the effect of quenching on the phase transformation temperatures. It was observed that the quaternary Cu–Al–Ni–Ti alloy is a high temperature shape memory alloy (HTSMA) and its transformation temperatures significantly were affected by heat treatments, e.g., the phase transformation temperatures increased via quenching in alcohol and iced brine by approximately 100 K. Moreover, optical microscopy (OM) and Scanning Electron Microscopy (SEM) images were taken to observe the changes in the microstructure after heat treatment. It was revealed that grain boundaries were more discernable in the samples that were quenched in alcohol and iced brine, also the volume fraction of martensite plates was increased. Crystal structures of samples at room temperature were determined by using X-ray diffractograms, whereby, the pattern showed the presence of β', γ2, and X phases, which are of martensite origin.

Sobre autores

F. Dagdelen

Department of Physics, Faculty of Science, Firat University

Autor responsável pela correspondência
Email: fethidagdelen@gmail.com
Turquia, Elazig

M. Kanca

Department of Physics, Faculty of Science, Firat University

Email: fethidagdelen@gmail.com
Turquia, Elazig

M. Kok

Department of Physics, Faculty of Science, Firat University

Email: fethidagdelen@gmail.com
Turquia, Elazig


Declaração de direitos autorais © Pleiades Publishing, Ltd., 2019

Este site utiliza cookies

Ao continuar usando nosso site, você concorda com o procedimento de cookies que mantêm o site funcionando normalmente.

Informação sobre cookies