Phase Composition, Structure, and Hardening of Alloys Containing 6% (Ca + Si) in the System Al–Ca–Si–Zr–Sc
- Авторлар: Belov N.1, Naumova E.1, Doroshenko V.1, Korotkova N.1
-
Мекемелер:
- MISiS National Research Technological University
- Шығарылым: Том 119, № 12 (2018)
- Беттер: 1184-1190
- Бөлім: Structure, Phase Transformations, and Diffusion
- URL: https://journals.rcsi.science/0031-918X/article/view/168019
- DOI: https://doi.org/10.1134/S0031918X18120037
- ID: 168019
Дәйексөз келтіру
Аннотация
Thermo-Calc calculations and experimental methods (optical and electron scanning microscopy, and electron microprobe analysis) were used to study the phase composition of alloys of the Al–Ca–Si–Sc–Zr system with the same scandium and zirconium contents (0.1 and 0.25 wt %, respectively) and the same total silicon and calcium content (6 wt %). It was shown that the hardening due to the precipitation of nanoparticles of the phase Al3(Zr, Sc)–L12 reaches a maximum after annealing at 300–450°C in alloys within the phase region (Al) + Al4Ca + Al2Si2Ca, where (Al) stands for a solid solution based on aluminum. In alloys within this region, almost all of the zirconium and scandium are contained in (Al), and the silicon content of the alloys is minimum. However, Zr and Sc additions have almost no effect on hardening in alloys within the (Al) + (Si) + Al2Si2Ca phase region. The aluminum–calcium eutectic has an essentially finer structure than that of aluminum–silicon.
Негізгі сөздер
Авторлар туралы
N. Belov
MISiS National Research Technological University
Хат алмасуға жауапты Автор.
Email: nikolay-belov@yandex.ru
Ресей, Moscow, 119049
E. Naumova
MISiS National Research Technological University
Email: nikolay-belov@yandex.ru
Ресей, Moscow, 119049
V. Doroshenko
MISiS National Research Technological University
Email: nikolay-belov@yandex.ru
Ресей, Moscow, 119049
N. Korotkova
MISiS National Research Technological University
Email: nikolay-belov@yandex.ru
Ресей, Moscow, 119049