Influence of megaplastic deformation on the structure and hardness of Al–Cu–Mg alloy after aging

Resumo

Methods of electron microscopy and X-ray diffraction have been used to investigate structural and phase transformations in the aluminum alloy of grade A2024 (Al–4.5 Cu–1.37 Mg–0.61 Mn–0.07 Si–0.27 Fe–0.02 Zn–0.02 Ti (wt %)) after aging and deformation by shear under high quasi-static pressure. It has been shown that the combination of two-stage aging with megaplastic deformation leads to the refinement of the structure to a nanolevel and to strengthening of the alloy (to an increase in the microhardness to 3000 MPa). The values of true deformation at which the deformation-induced dissolution of the particles of the strengthening S phase occurs have been determined.