Ferritic Decomposition in Fe–36Ni–3Cr Invar Alloy

V. V. Sagaradze; N. V. Kataeva; V. A. Zavalishin; A. V. Litvinov; M. F. Klyukina

doi:10.1134/S0031918X19100119

Ferritic Decomposition in Fe–36Ni–3Cr Invar Alloy

作者: Sagaradze V.V.¹^,2, Kataeva N.V.¹, Zavalishin V.A.¹, Litvinov A.V.¹, Klyukina M.F.¹
隶属关系:
1. Mikheev Institute of Metal Physics, Ural Branch, Russian Academy of Sciences
2. Ural Federal University Named after the First President of Russia B.N. Yeltsin
期: 卷 120, 编号 10 (2019)
页面: 956-961
栏目: Structure, Phase Transformations, and Diffusion
URL: https://journals.rcsi.science/0031-918X/article/view/168741
DOI: https://doi.org/10.1134/S0031918X19100119
ID: 168741

如何引用文章

全文:

开放存取

##reader.subscriptionAccessGranted##
受限制的访问

订阅存取

详细
作者简介
参考
补充文件
统计

详细

Nickel redistribution and austenite decomposition into ferrite with the formation of up to 15% α‑ferrite crystals 10–100 nm in size in a fairly stable Fe–36Ni–3Cr invar alloy were found. The austenite decomposition during heating in a 250–400°C temperature range is intensified by preliminary strong plastic deformation by rolling or shearing under high pressure.

关键词

austenitic alloy, ferrite, magnetic transformation, deformation, nickel segregation, electron microscopy, magnetometry

作者简介

V. Sagaradze

Mikheev Institute of Metal Physics, Ural Branch, Russian Academy of Sciences; Ural Federal University Named after the First President of Russia B.N. Yeltsin

编辑信件的主要联系方式.
Email: vsagaradze@imp.uran.ru
俄罗斯联邦, Ekaterinburg, 620108; Ekaterinburg, 620002