Embrittlement and conditions of the optimization of magnetic properties in the amorphous alloy Co69Fe3.7Cr3.8Si12.5B11 in the absence of a viscous–brittle transition

Abstract

The influence of the holding time upon annealing on the temperature of the viscous–brittle transition (temperature of embrittlement) T_f in a cobalt-based amorphous alloy of the composition Co₆₉Fe_3.7Cr_3.8Si_12.5B₁₁ with a very low saturation magnetostriction λ_s (<10^–7) has been studied. It has been established that the dependence of the embrittlement temperature T_f on the of time of holding t_a can be described by an Arrhenius equation and that the embrittlement at the annealing temperatures above and below 300°C is described by different kinetic parameters. In the alloy under study, irrespective of the holding time, embrittlement occurs in a very narrow range of annealing temperatures, which does not exceed 5 K. Based on the experimental data on the evolution of the hysteresis magnetic properties upon the isochronous annealings and upon the isothermal holding, the regime of heat treatment that ensures a very high (about 50000) magnitude of the permeability µ₅ (H = 5 mOe, f = 1 kHz) without the transition of the alloy into a brittle state has been determined.