Correction of the band gap of Y2O3:Eu3+ phosphor

Abstract

Submicron samples of Y₂O₃:Eu³⁺ phosphor with elevated photoluminescence (PL) efficiency and activator concentration of 9 at % obtained by the sol–gel method were investigated by diffuse reflection spectroscopy and PL spectroscopy. It is found that the diffuse reflection spectrum in the vicinity of the fundamental absorption edge (<300 nm) is distorted by the superposition of the PL of Eu³⁺ ions, as a result of which the calculated value of optical band gap E_g of the Y₂O₃ matrix is overestimated. An algorithm for eliminating the PL influence on the absorption edge is proposed, and the correct E_g values are found to be 4.61 ± 0.12 and 4.50 ± 0.12 eV for annealing at 700 and 1300°C, respectively.