Surface Hardening of Titanium Under Non-Vacuum Electron-Beam Cladding of an Aluminum-Containing Powder Mixture


如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅存取

详细

Special features of the structure of surface layers formed on billets of commercial-purity titanium VT1-0 by cladding a powder aluminum-titanium mixture with an electron beam removed into air atmosphere are studied. X-ray phase analysis and transmission electron microscopy are used to show that the material remelted by the electron beam is Ti3Al titanium aluminide. The hardness of the deposited layer is 540 – 610 HV. The behavior of the material is studied under the conditions of sliding friction and friction against fixed abrasive particles. The results reflect decrease in the friction factor and increase in the wear resistance of the clad material as compared to commercially pure titanium.

作者简介

I. Bataev

Novosibirsk State Technical University

编辑信件的主要联系方式.
Email: i.bataev@corp.nstu.ru
俄罗斯联邦, Novosibirsk

D. Lazurenko

Novosibirsk State Technical University

Email: i.bataev@corp.nstu.ru
俄罗斯联邦, Novosibirsk

M. Golkovskii

Institute of Nuclear Physics of the Siberian Branch of the Russian Academy of Sciences

Email: i.bataev@corp.nstu.ru
俄罗斯联邦, Novosibirsk

A. Bataev

Novosibirsk State Technical University

Email: i.bataev@corp.nstu.ru
俄罗斯联邦, Novosibirsk

O. Matts

Novosibirsk State Technical University

Email: i.bataev@corp.nstu.ru
俄罗斯联邦, Novosibirsk

补充文件

附件文件
动作
1. JATS XML

版权所有 © Springer Science+Business Media, LLC, part of Springer Nature, 2019