Мақаланы E-mail арқылы жіберу Features of Intermetallic Alloy TNM-B1 High-Temperature Oxidation
- Авторлар: Smyslov A.M.1, Bybin A.A.1, Dautov S.S.1
-
Мекемелер:
- Ufa State Aviation Technical University
- Шығарылым: Том 58, № 5-6 (2016)
- Беттер: 268-272
- Бөлім: Article
- URL: https://journals.rcsi.science/0026-0673/article/view/234963
- DOI: https://doi.org/10.1007/s11041-016-0001-0
- ID: 234963
Дәйексөз келтіру
Ашық рұқсат
Рұқсат берілді
Тек жазылушылар үшін
Аннотация
Features of intermetallic alloy based on titanium aluminide high-temperature oxidation at 800 – 850°C are studied. A mathematical dependence is obtained for oxidation rate on test duration. The structure and composition of an oxide layer formed during high-temperature oxidation are studied. It is shown that under operating conditions at the maximum working temperatures the intermetallic alloy exhibits low heat resistance.
Авторлар туралы
A. Smyslov
Ufa State Aviation Technical University
Email: anbybin@yandex.ru
Ресей, Ufa
A. Bybin
Ufa State Aviation Technical University
Хат алмасуға жауапты Автор.
Email: anbybin@yandex.ru
Ресей, Ufa
S. Dautov
Ufa State Aviation Technical University
Email: anbybin@yandex.ru
Ресей, Ufa
Қосымша файлдар