Oxidative Condensation of Methane on Sr2 –xLaxTiO4 Catalysts: Effect of the Degree of Substitution of Sr and La
- Authors: Petrov R.V.1, Ivanova Y.A.1, Reshetnikov S.I.1, Isupova L.A.1
-
Affiliations:
- Boreskov Institute of Catalysis, Siberian Branch, Russian Academy of Sciences
- Issue: Vol 60, No 6 (2019)
- Pages: 862-867
- Section: Article
- URL: https://journals.rcsi.science/0023-1584/article/view/164317
- DOI: https://doi.org/10.1134/S0023158419030108
- ID: 164317
Cite item
Abstract
The Sr2 –xLaxTiO4 (x = 0–2.0) catalysts were synthesized based on strontium titanate with a layered perovskite structure. The effect of the degree of substitution of La for Sr on the physicochemical (phase composition and textural characteristics) and catalytic properties of oxides in the oxidative condensation of methane at temperatures of 700–800°C were studied. It was found that multiphase Sr2 – xLaxTiO4 samples with the degree of substitution x = 0.8–1.8 were most active and selective in the test reaction; this was likely related to the presence of lanthanum oxide and strontium oxide impurities in them, their optimum distribution over the surface, and the specific surface area.
About the authors
R. V. Petrov
Boreskov Institute of Catalysis, Siberian Branch, Russian Academy of Sciences
Author for correspondence.
Email: petrov@catalysis.ru
Russian Federation, Novosibirsk, 630090
Yu. A. Ivanova
Boreskov Institute of Catalysis, Siberian Branch, Russian Academy of Sciences
Email: petrov@catalysis.ru
Russian Federation, Novosibirsk, 630090
S. I. Reshetnikov
Boreskov Institute of Catalysis, Siberian Branch, Russian Academy of Sciences
Email: petrov@catalysis.ru
Russian Federation, Novosibirsk, 630090
L. A. Isupova
Boreskov Institute of Catalysis, Siberian Branch, Russian Academy of Sciences
Email: petrov@catalysis.ru
Russian Federation, Novosibirsk, 630090