Electrical Conductivity and Electrochemical Characteristics of Na3V2(PO4)3-Based NASICON-Type Materials

详细

NASICON-type materials with the compositions Na₃V_2–xAl_x(PO₄)₃, Na₃V_{2 - x}Fe_x(PO₄)₃, Na_{3 + x}V_2–xNi_x(PO₄)₃, and Na₃V_{2 - x}Cr_x(PO₄)₃ (x = 0, 0.03, 0.05, and 0.1) have been prepared and characterized by X-ray diffraction analysis, electron microscopy, and impedance spectroscopy. The results demonstrate that the highest electrical conductivity among the samples studied is offered by the material doped with 5% Fe: Na₃V_1.9Fe_0.1(PO₄)₃. The activation energy for low-temperature conduction in the doped materials decreases from 84 ± 2 to 54 ± 1 kJ/mol and that for high-temperature conduction is ~33 kJ/mol. The discharge capacity of Na₃V_1.9Fe_0.1(PO₄)₃/C under typical working conditions of cathodes of sodium ion batteries has been shown to exceed that of Na₃V₂(PO₄)₃/C. The capacity of the more porous material prepared by the Pechini process (Na₃V_1.9Fe_0.1(PO₄)₃/C-{II}) approaches the theoretical one at a low charge–discharge rate and retains its high level as the charge rate is raised (its discharge capacity was 117.6, 108.8, and 82.6 mAh/g at a discharge rate of 0.1C, 2C, and 8C, respectively).