Effect of chemical modification conditions on the sintering behavior of TiC powders


如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅存取

详细

Dense ceramics have been produced from a chemically modified titanium carbide powder. Chemical modification was carried out by siliciding titanium carbide powder in a gaseous SiO atmosphere at 1350°C. This treatment produced a Ti3SiC2 layer (up to 19 wt %) on the surface of the TiC particles. Hot pressing at a temperature of 1600°C and pressures from 10 to 20 MPa ensured effective densification of the modified powders. The density of the resultant material reaches 4.8 g/cm3, with a residual porosity under 2%. Its bending strength and fracture toughness are 330 ± 50 MPa and 6.2 ± 0.6 MPa m1/2, respectively.

作者简介

E. Istomina

Institute of Chemistry, Komi Scientific Center, Ural Branch

编辑信件的主要联系方式.
Email: Istomina-ei@chemi.komisc.ru
俄罗斯联邦, Pervomaiskaya ul. 48, Syktyvkar, Komi Republic, 167982

P. Istomin

Institute of Chemistry, Komi Scientific Center, Ural Branch

Email: Istomina-ei@chemi.komisc.ru
俄罗斯联邦, Pervomaiskaya ul. 48, Syktyvkar, Komi Republic, 167982

A. Nadutkin

Institute of Chemistry, Komi Scientific Center, Ural Branch

Email: Istomina-ei@chemi.komisc.ru
俄罗斯联邦, Pervomaiskaya ul. 48, Syktyvkar, Komi Republic, 167982

V. Grass

Institute of Chemistry, Komi Scientific Center, Ural Branch

Email: Istomina-ei@chemi.komisc.ru
俄罗斯联邦, Pervomaiskaya ul. 48, Syktyvkar, Komi Republic, 167982

补充文件

附件文件
动作
1. JATS XML

版权所有 © Pleiades Publishing, Ltd., 2016