Influence of isovalent and heterovalent substitution for Bi3+ and Fe3+ on the properties of Bi2Fe4O9-based solid solutions

Аннотация

Bi_2–хLa_хFe₄O₉ and Bi₂Fe_4–2xTi_xCo_xO₉ ferrites have been prepared by solid-state reactions at a temperature of 1073 K. X-ray diffraction data indicate that, in the Bi_2–хLa_хFe₄O₉ system, the limiting degree of La³⁺ substitution for Bi³⁺ ions in Bi₂Fe₄O₉ does not exceed 0.05 and that the limiting degree of substitution in the Bi₂Fe_4–2xTi_xCo_xO₉ system lies in the range 0.05 < x < 0.1. The specific magnetization and specific magnetic susceptibility of the samples have been measured at temperatures from 5 to 300 K in a magnetic field of 0.86 T. The field dependences of magnetization obtained for the Bi_2–хLa_хFe₄O₉ and Bi₂Fe_4–2xTi_xCo_xO₉ ferrites at temperatures of 300 and 5 K demonstrate that partial isovalent substitution of La³⁺ for Bi³⁺ ions in Bi₂Fe₄O₉ and heterovalent substitution of Ti⁴⁺ and Co²⁺ ions for two Fe³⁺ ions leads to partial breakdown of the antiferromagnetic state and nucleation of a ferromagnetic state.