Preparation of fine-grained ceramics by hot-pressing of Ce0.09Zr0.91O2/MgO/Al2O3 nanopowder

详细

We have studied the effect of hot-pressing conditions (different pressure rise rates and isothermal holding temperatures in the range 1450–1550°C) on the microstructure of ceramics produced from nanopowder with the composition Ce_0.09Zr_0.91O₂/MgAl₆O₁₀/γ-Al₂O₃ (20.6, 37.4, and 42.0 wt %, respectively). Firing at 1450°C for 1 h made it possible to obtain fine-grained ceramics with less than 3 μm in grain size. The compaction pressure rise rate was shown to be a key parameter under such thermal conditions (20 + 10°C/min → 1450°C). Grain growth was prevented most effectively when the maximum load, 30 MPa, was reached at a temperature of 1000°C. Under such conditions, the grain size was 0.4–0.8 μm and the relative density reached 98.8%.