Effect of Barothermal Processing on the Solid-State Formation of the Structure and Properties of 16 at % Si–Al Hypereutectic Alloy

Аннотация

We describe barothermal processing (hot isostatic pressing) of a 16 at % Si–Al binary alloy for 3 h at a temperature of 560°C and pressure of 100 MPa for 3 h, in combination with measurements of heat effects during cooling. The results demonstrate that this processing leads to the fragmentation of the silicon structural constituent and ensures a high degree of homogenization of the as-prepared alloy. Heat treatment of the 16 at % Si–Al alloy at 560°C and a pressure of 100 MPa leads to a thermodynamically driven enhanced silicon dissolution, up to ~10 at %, in the aluminum matrix, resulting in the formation of a supersaturated solid solution, which subsequently decomposes during cooling. We analyze the complete porosity elimination process, which makes it possible to obtain a material with 100% relative density. According to differential barothermal analysis, microstructural analysis, and scanning and transmission electron microscopy data, barothermal processing of the 16 at % Si–Al alloy produces a bimodal size distribution of the silicon phase constituent: microparticles 3.6 μm in average size and nanoparticles down to ~1 nm in diameter. The Al matrix has been shown to contain a high density of edge dislocations. Barothermal processing reduces the thermal expansion coefficient and microhardness of the hypereutectic alloy. We conclude that solid-state barothermal processing is an effective tool for completely eliminating microporosity from the 16 at % Si–Al alloy, reaching a high degree of homogenization, and controlling the microstructure of the alloy, in particular by producing high dislocation density in the aluminum matrix.