Influence of the Sodium Niobate Addition on the Sintering and Properties of Zirconia Ceramics
- Authors: Smirnov V.V.1, Smirnov S.V.1, Obolkina T.O.1, Goldberg M.A.1, Antonova O.S.1, Barinov S.M.1
-
Affiliations:
- Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences
- Issue: Vol 486, No 1 (2019)
- Pages: 141-143
- Section: Chemical Technology
- URL: https://journals.rcsi.science/0012-5008/article/view/154443
- DOI: https://doi.org/10.1134/S0012500819050033
- ID: 154443
Cite item
Abstract
The sintering, microstructure, and phase composition of zirconia ceramics containing a sodium niobate addition have been studied. It has been shown that the addition leads to a decrease in the sintering temperature to 1400°С. The resulting materials are characterized by a high content of the tetragonal phase, a fine-crystalline structure, and a high flexural strength up to 440 MPa. The developed low-temperature materials can be used in dentistry as ceramic crowns.
About the authors
V. V. Smirnov
Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences
Author for correspondence.
Email: smirnov2007@mail.ru
Russian Federation, Moscow, 119334
S. V. Smirnov
Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences
Email: smirnov2007@mail.ru
Russian Federation, Moscow, 119334
T. O. Obolkina
Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences
Email: smirnov2007@mail.ru
Russian Federation, Moscow, 119334
M. A. Goldberg
Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences
Email: smirnov2007@mail.ru
Russian Federation, Moscow, 119334
O. S. Antonova
Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences
Email: smirnov2007@mail.ru
Russian Federation, Moscow, 119334
S. M. Barinov
Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences
Email: smirnov2007@mail.ru
Russian Federation, Moscow, 119334