Production of High-Flexural-Strength Corundum Ceramics

详细

A new method was proposed to produce high-flexural-strength corundum ceramics from α-Al₂O₃ samples synthesized by heat treatment of boehmite AlOOH at 1300°C for 5 h. It was shown that hydrothermal treatment of MDGA-grade hydrargillite at 200°C in a 0.4 wt % magnesium acetate solution for 3 days gives finely crystalline boehmite, which is a feedstock for synthesizing corundum ceramics with a flexural strength of 400 MPa.