Arsenide-silicate glasses formed by oxidation of sih4 and ash3 to diffuse arsenic into si and sio2
- Autores: Mustafayev H.A.1, Mustafayev A.H.1, Zdravomyslov D.M.1
-
Afiliações:
- Kabardino-Balkarian State University named after H.M. Berbekova.
- Edição: Volume 15, Nº 1 (2025)
- Páginas: 16-20
- Seção: Physics
- URL: https://journals.rcsi.science/2221-7789/article/view/358102
- ID: 358102
Citar
Texto integral
Resumo
The paper studied arsenide-silicate glasses formed by oxidation of SiH4 and AsH3. It has been shown that the precipitation rate decreases sharply when the concentration of AsH3 in the mixture of reagents is more than 10 mol%. The diffusion of arsenic through barrier oxide and without barrier oxide was studied using oxygen O2 and argon Ar as a diffusion medium. It has been shown that the use of oxygen O2 instead of argon Ar as a diffusion medium changes the nature of defects, leads to an increase in the depths of transitions and the surface concentration of arsenic As in diffusion layers. A connection has been found between the concentration of As2O3 in glasses and the tendency to form defects in glass during heat treatment.
Sobre autores
Hasan Mustafayev
Kabardino-Balkarian State University named after H.M. Berbekova.
Autor responsável pela correspondência
Email: zoone@mail.ru
Department of Electronics and Digital Information Technologies, Institute of Electronics, Robotics and Artificial Intelligence Rússia
Arslan Mustafayev
Kabardino-Balkarian State University named after H.M. Berbekova.
Email: zoone@mail.ru
Doctor of Technical Sciences, Professor of the Department of Information Technology and Information Security. Rússia
Denis Zdravomyslov
Kabardino-Balkarian State University named after H.M. Berbekova.
Email: zoone@mail.ru
Graduate student of 2 years of study in the specialty: Electronic component base of micro- and electronics, quantum devices. Rússia
Arquivos suplementares