Ceramics based on calcium phosphate powder synthesized from calcium saccharate and ammonium hydrophosphate
- Авторы: Safronova T.1, Kazakova G.1, Yevdokimov P.1, Shatalova T.1, Knotko A.1, Korotkova A.1, Putlyayev V.1
-
Учреждения:
- Moscow State University
- Выпуск: Том 7, № 4 (2016)
- Страницы: 635-640
- Раздел: Article
- URL: https://journals.rcsi.science/2075-1133/article/view/205634
- DOI: https://doi.org/10.1134/S2075113316040316
- ID: 205634
Цитировать
Аннотация
A microporous ceramic with a pore size ranging from 1 to 6 μm and a relative density up to 56% was obtained from the calcium phosphate powder synthesized from aqueous solutions of monocalcium saccharate (CaC12H22O11) and ammonium hydrophosphate. The composition of the synthesized nanosized powder is found to include hydroxyapatite and sucrose. The phase composition of the ceramic after calcination in the range from 900 to 1200°C is represented by β-tricalcium phosphate and hydroxyapatite. The resulting ceramic material can be recommended for the manufacture of bone implants.
Ключевые слова
Об авторах
T. Safronova
Moscow State University
Автор, ответственный за переписку.
Email: t3470641@yandex.ru
Россия, Moscow
G. Kazakova
Moscow State University
Email: t3470641@yandex.ru
Россия, Moscow
P. Yevdokimov
Moscow State University
Email: t3470641@yandex.ru
Россия, Moscow
T. Shatalova
Moscow State University
Email: t3470641@yandex.ru
Россия, Moscow
A. Knotko
Moscow State University
Email: t3470641@yandex.ru
Россия, Moscow
A. Korotkova
Moscow State University
Email: t3470641@yandex.ru
Россия, Moscow
V. Putlyayev
Moscow State University
Email: t3470641@yandex.ru
Россия, Moscow