全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅存取

详细

New solid solutions Ca3B2 + xSi1–xO8–x/2 based on monoclinic borosilicate β-Ca3B2SiO8 are prepared using crystallization from a melt. The homogeneity range of solid solutions (0 < х ≤ 0.86) is determined and the thermal behavior of solid solution Ca3B2.4Si0.6O7.8 is studied using high-temperature X-ray powder diffraction: a reversible β ↔ α polymorphic transition is discovered in the solid solution (х = 0.4) at 550°C, decomposition begins in the solid state above 940°C with the formation of CaSiO3. The thermal expansion of both modifications is anisotropic: 20–540°C (α11 = 17, α22 = 16, α33 = 0, αV = 32 × 10−6°C−1) and 560–900°C (α11 = 15, α22 = 24, α33 = 3, and αV = 42 × 10−6°C−1).

作者简介

M. Krzhizhanovskaya

St. Petersburg State University

Email: rimma_bubnova@mail.ru
俄罗斯联邦, St. Petersburg, 199034

R. Bubnova

Grebenshchikov Institute of Silicate Chemistry; St. Petersburg State University

编辑信件的主要联系方式.
Email: rimma_bubnova@mail.ru
俄罗斯联邦, St. Petersburg, 199034; St. Petersburg, 199034

V. Yukhno

Grebenshchikov Institute of Silicate Chemistry

Email: rimma_bubnova@mail.ru
俄罗斯联邦, St. Petersburg, 199034

补充文件

附件文件
动作
1. JATS XML

版权所有 © Pleiades Publishing, Ltd., 2017