Sol-Gel Synthesis, Thermal Behavior of Nanopowders and Chemical Stability of La1 – xHoxPO4 Ceramic Matrices
- Autores: Mezentseva L.1, Osipov A.1, Ugolkov V.1, Akatov A.2, Doilnitsyn V.2, Maslennikova T.1, Yakovlev A.1
-
Afiliações:
- Grebenshchikov Institute of Silicate Chemistry
- Saint-Petersburg State Institute of Technology (Technical University)
- Edição: Volume 44, Nº 5 (2018)
- Páginas: 440-449
- Seção: Article
- URL: https://journals.rcsi.science/1087-6596/article/view/216733
- DOI: https://doi.org/10.1134/S1087659618050127
- ID: 216733
Citar
Resumo
Nanosized powders of orthophosphates in the LaPO4–HoPO4–H2O system have been synthesized to determine the mutual solubility of LaPO4 · nH2O and HoPO4 · nH2O initial components and to obtain ceramic matrices by sintering them. Formation of hexagonal, monoclinic or tetragonal solid solutions was revealed, and their limits and thermal stability were determined. A series of limited hexagonal LaPO4 · nH2O-based solid solutions was observed within the 0 ≤ x ≤ 0.6 concentration range up to 600°C. Further they transformed to monoclinic LaPO4-based form within the 0 ≤ x ≤ 0.3 concentration range. Solubility of LaPO4 · nH2O and LaPO4 in tetragonal HoPO4(· nH2O) is lower (≤10 mol %). Specific surface area of La1–xHoxPO4 · nH2O powders was in the range of 90.5–165.0 m2/g depending on x. Leaching rate of La3+ and Ho3+ from La1–xHoxPO4 matrices in nitric acid solution (pH 1–2) was determined to be 10–5–10–2 g/(cm2 day) for both ions.
Sobre autores
L. Mezentseva
Grebenshchikov Institute of Silicate Chemistry
Autor responsável pela correspondência
Email: la_mez@mail.ru
Rússia, St. Petersburg, 199034
A. Osipov
Grebenshchikov Institute of Silicate Chemistry
Email: la_mez@mail.ru
Rússia, St. Petersburg, 199034
V. Ugolkov
Grebenshchikov Institute of Silicate Chemistry
Email: la_mez@mail.ru
Rússia, St. Petersburg, 199034
A. Akatov
Saint-Petersburg State Institute of Technology (Technical University)
Email: la_mez@mail.ru
Rússia, St. Petersburg, 190013
V. Doilnitsyn
Saint-Petersburg State Institute of Technology (Technical University)
Email: la_mez@mail.ru
Rússia, St. Petersburg, 190013
T. Maslennikova
Grebenshchikov Institute of Silicate Chemistry
Email: la_mez@mail.ru
Rússia, St. Petersburg, 199034
A. Yakovlev
Grebenshchikov Institute of Silicate Chemistry
Email: la_mez@mail.ru
Rússia, St. Petersburg, 199034