Enviar artigo por via de e-mail Effect of thermal treatment modes on ion-conducting properties of lithium-aluminum titanophosphate
- Autores: Kunshina G.B.1, Bocharova I.V.1, Ivanenko V.I.1
-
Afiliações:
- Tananaev Institute of Chemistry and Technology of Rare Elements and Mineral Raw Materials, Kola Scientific Center
- Edição: Volume 90, Nº 3 (2017)
- Páginas: 374-379
- Seção: Applied Electrochemistry and Metal Corrosion Protection
- URL: https://journals.rcsi.science/1070-4272/article/view/214764
- DOI: https://doi.org/10.1134/S1070427217030089
- ID: 214764
Citar
Acesso aberto
Acesso está concedido
Somente assinantes
Resumo
Dependence of the density of the Li1.3Al0.3Ti1.7(PO4)3 (LATP) ceramic on thermal treatment modes was studied. The conditions in which ceramic samples with density exceeding 90% are obtained were determined. It was found that the bulk ionic conductivity of LATP upon sintering at 1000°C for 2–6 h is (1.1–1.3) × 10–3 S cm–1 at 20°C, which corresponds to the maximum values for lithium-aluminum titanophosphate.
Sobre autores
G. Kunshina
Tananaev Institute of Chemistry and Technology of Rare Elements and Mineral Raw Materials, Kola Scientific Center
Autor responsável pela correspondência
Email: kunshina@chemy.kolasc.net.ru
Rússia, Akademgorodok 26a, Apatity, 184209
I. Bocharova
Tananaev Institute of Chemistry and Technology of Rare Elements and Mineral Raw Materials, Kola Scientific Center
Email: kunshina@chemy.kolasc.net.ru
Rússia, Akademgorodok 26a, Apatity, 184209
V. Ivanenko
Tananaev Institute of Chemistry and Technology of Rare Elements and Mineral Raw Materials, Kola Scientific Center
Email: kunshina@chemy.kolasc.net.ru
Rússia, Akademgorodok 26a, Apatity, 184209
Arquivos suplementares