Мақаланы E-mail арқылы жіберу Formation and thermal properties of nanocrystalline Bi4Ti3O12
- Авторлар: Lomanova N.A.1, Tomkovich M.V.1, Ugolkov V.L.2, Gusarov V.V.1
-
Мекемелер:
- Ioffe Institute
- Grebenshchikov Institute of Silicate Chemistry
- Шығарылым: Том 90, № 6 (2017)
- Беттер: 831-837
- Бөлім: Inorganic Synthesis and Industrial Inorganic Chemistry
- URL: https://journals.rcsi.science/1070-4272/article/view/214944
- DOI: https://doi.org/10.1134/S1070427217060015
- ID: 214944
Дәйексөз келтіру
Ашық рұқсат
Рұқсат берілді
Тек жазылушылар үшін
Аннотация
Mechanism by which nanocrystalline Bi4Ti3O12 is formed in thermal treatment of coprecipitated hydroxides was studied. It was shown that the onset of the active formation is correlated with the melting point of the surface phase based on bismuth oxide. The technological synthesis parameters of Bi4Ti3O12, at which crystallite sizes in the range 35–60 nm are provided, were determined.
Авторлар туралы
N. Lomanova
Ioffe Institute
Хат алмасуға жауапты Автор.
Email: natus@mail.ioffe.ru
Ресей, ul. Politechnicheskaya 26, St. Petersburg, 194021
M. Tomkovich
Ioffe Institute
Email: natus@mail.ioffe.ru
Ресей, ul. Politechnicheskaya 26, St. Petersburg, 194021
V. Ugolkov
Grebenshchikov Institute of Silicate Chemistry
Email: natus@mail.ioffe.ru
Ресей, ul. Tiflisskaya 3/6, St. Petersburg, 199034
V. Gusarov
Ioffe Institute
Email: natus@mail.ioffe.ru
Ресей, ul. Politechnicheskaya 26, St. Petersburg, 194021
Қосымша файлдар