High-temperature synthesis of pitch
- 作者: Petrovykh A.1, Abaturov A.1, Moskalev I.1, Kiselkov D.1, Astaf’eva S.1, Vinokurov A.2
-
隶属关系:
- Institute of Engineering Chemistry, Ural Branch
- Perm Polytechnic University
- 期: 卷 60, 编号 2 (2017)
- 页面: 75-79
- 栏目: Chemistry
- URL: https://journals.rcsi.science/1068-364X/article/view/226187
- DOI: https://doi.org/10.3103/S1068364X17020065
- ID: 226187
如何引用文章
详细
The heat treatment of the anthracene fraction of coal tar under pressure is considered. In the production of synthetic pitch, the duration of the process is varied from 10 to 80 min, at a temperature of 500°C and a pressure of 3 MPa. Kinetic data for the formation of γ and α1 fractions show that the polycondensation of the γ fraction is of second order, while the formation of the α1 fraction is of zero order. Pitch obtained with holding for 10–40 min does not contain the α1 fraction. Extending the process beyond 30 min does not affect the removal of heteroatoms. IR spectroscopic data indicate that dealkylation predominates for the first 40 min. Then the process slows, and compaction develops.
作者简介
A. Petrovykh
Institute of Engineering Chemistry, Ural Branch
编辑信件的主要联系方式.
Email: petrovyhnastya@mail.ru
俄罗斯联邦, Perm
A. Abaturov
Institute of Engineering Chemistry, Ural Branch
Email: petrovyhnastya@mail.ru
俄罗斯联邦, Perm
I. Moskalev
Institute of Engineering Chemistry, Ural Branch
Email: petrovyhnastya@mail.ru
俄罗斯联邦, Perm
D. Kiselkov
Institute of Engineering Chemistry, Ural Branch
Email: petrovyhnastya@mail.ru
俄罗斯联邦, Perm
S. Astaf’eva
Institute of Engineering Chemistry, Ural Branch
Email: petrovyhnastya@mail.ru
俄罗斯联邦, Perm
A. Vinokurov
Perm Polytechnic University
Email: petrovyhnastya@mail.ru
俄罗斯联邦, Perm