Formation of the structure and phase composition of the Ti–Al–Ta-based materials

Аннотация

The experiments on the fabrication of materials based on the Ti–3Al–0.5Ta and 3Ti–2Al–Ta systems by self-propagating high-temperature synthesis (SHS) are performed. The influence of the composition of the initial mixture, dispersity of powders, and preliminary mechanical activation on the phase composition and structure of the SHS product is investigated. The optimal ratio between the mechanically activated and initial powder in a mixture for the synthesis of materials is determined. The dependence of the structure of final products on the structure of initial powders is established. The use of porous tantalum leads to the formation of the intermetallic matrix based on titanium aluminide with the uniform distribution of Ta particles. It is noteworthy that tantalum powders of both studied series (which differ by dispersity and morphology) partially reacted already at the stage of mechanical activation with the formation of the Al₂Ta phase. It is shown that aluminum plays the leading role in processes of mechanical activation in Ti–Al–Ta reaction mixtures. Indeed, a considerable rise of unreacted tantalum particles in the microstructure of sintered samples is observed with a decrease in the amount of aluminum in the reaction mixture.