- Авторы: Ivanets A.1, Katsoshvili L.1, Krivoshapkin P.2,3, Prozorovich V.1, Kuznetsova T.1, Krivoshapkina E.2,3, Radkevich A.4, Zarubo A.4
-
Учреждения:
- Institute of General and Inorganic Chemistry
- Institute of Chemistry, Komi Scientific Center, Ural Branch
- University of Information Technologies, Mechanics, and Optics
- Joint Institute for Power and Nuclear Research—Sosny
- Выпуск: Том 59, № 3 (2017)
- Страницы: 264-271
- Раздел: Article
- URL: https://journals.rcsi.science/1066-3622/article/view/223913
- DOI: https://doi.org/10.1134/S1066362217030080
- ID: 223913
Цитировать
Аннотация
Sorption of stable and radioactive strontium ions onto mesoporous manganese oxide of OMS-2 type, prepared by the sol–gel method via reduction of potassium permanganate with polyvinyl alcohol in aqueous medium, was studied. The influence exerted by the pore structure parameters and by the phase and chemical composition of manganese oxide on its sorption properties and selectivity to Sr ions was examined. Manganese oxide samples prepared using a 0.1 wt % KMnO4 solution exhibit the highest values of the sorption capacity for Sr, about 100–150 mg g–1, and of the Sr distribution coefficient, Kd = (11.5–19.5) × 103 cm3 g–1. Introduction of 0.1 M NaCl into this solution considerably decreases the sorption of stable Sr ions, and for all the samples the sorption capacity is 25–35 mg g–1. On the other hand, for the most active sorbents the distribution coefficient in the presence of 0.1 M NaCl increases by a factor of approximately 8–10 relative to distilled water and reaches (91–208) × 103 cm3 g–1. Introduction of 0.05 M CaCl2 also decreases the Sr uptake, and the sorption capacity of the most active sorbents for stable Sr ions is 25–35 mg g–1 at Kd (85Sr) equal to (0.14–0.35) × 103 cm3 g–1.
Ключевые слова
Об авторах
A. Ivanets
Institute of General and Inorganic Chemistry
Автор, ответственный за переписку.
Email: Andreiivanets@yandex.ru
Белоруссия, ul. Surganova 9/1, Minsk, 220072
L. Katsoshvili
Institute of General and Inorganic Chemistry
Email: Andreiivanets@yandex.ru
Белоруссия, ul. Surganova 9/1, Minsk, 220072
P. Krivoshapkin
Institute of Chemistry, Komi Scientific Center, Ural Branch; University of Information Technologies, Mechanics, and Optics
Email: Andreiivanets@yandex.ru
Россия, ul. Pervomaiskaya 48, Syktyvkar, Komi Republic, 167982; Birzhevaya liniya 16, St. Petersburg, 199034
V. Prozorovich
Institute of General and Inorganic Chemistry
Email: Andreiivanets@yandex.ru
Белоруссия, ul. Surganova 9/1, Minsk, 220072
T. Kuznetsova
Institute of General and Inorganic Chemistry
Email: Andreiivanets@yandex.ru
Белоруссия, ul. Surganova 9/1, Minsk, 220072
E. Krivoshapkina
Institute of Chemistry, Komi Scientific Center, Ural Branch; University of Information Technologies, Mechanics, and Optics
Email: Andreiivanets@yandex.ru
Россия, ul. Pervomaiskaya 48, Syktyvkar, Komi Republic, 167982; Birzhevaya liniya 16, St. Petersburg, 199034
A. Radkevich
Joint Institute for Power and Nuclear Research—Sosny
Email: Andreiivanets@yandex.ru
Белоруссия, Minsk, 220109
A. Zarubo
Joint Institute for Power and Nuclear Research—Sosny
Email: Andreiivanets@yandex.ru
Белоруссия, Minsk, 220109