The formation of nanostructured carbon material on a ferrocene-containing polymer surface induced by a high-power ion beam
- Авторлар: Kovivchak V.1,2, Kryazhev Y.2,3, Zapevalova E.3
-
Мекемелер:
- Omsk State University
- Omsk Scientific Center, Siberian Branch
- Institute of Hydrocarbon Processing, Omsk Scientific Center, Siberian Branch
- Шығарылым: Том 42, № 2 (2016)
- Беттер: 153-155
- Бөлім: Article
- URL: https://journals.rcsi.science/1063-7850/article/view/197133
- DOI: https://doi.org/10.1134/S1063785016020103
- ID: 197133
Дәйексөз келтіру
Аннотация
The surface morphology and the composition of polymer layers based on chlorinated polyvinylchloride with addition of ferrocene (up to 10% of the polymer mass) subject to the action of a nanosecond high-power ion beam are studied. It is demonstrated that carbon material in the form of nanofibers with an average diameter of 80 nm and a length of up to 10 μm is formed on a surface singly irradiated by such beam with a current density of ∼100 A/cm2. A possible mechanism of the observed phenomenon is discussed.
Негізгі сөздер
Авторлар туралы
V. Kovivchak
Omsk State University; Omsk Scientific Center, Siberian Branch
Хат алмасуға жауапты Автор.
Email: kvs@univer.omsk.su
Ресей, Omsk, 664077; Omsk, 644024
Yu. Kryazhev
Omsk Scientific Center, Siberian Branch; Institute of Hydrocarbon Processing, Omsk Scientific Center, Siberian Branch
Email: kvs@univer.omsk.su
Ресей, Omsk, 644024; Omsk, 634055
E. Zapevalova
Institute of Hydrocarbon Processing, Omsk Scientific Center, Siberian Branch
Email: kvs@univer.omsk.su
Ресей, Omsk, 634055