The Influence of the Cobalt Content on the Strength Properties of Tungsten Carbide Ceramics under Dynamic Loads
- 作者: Savinykh A.1,2, Mandel K.3, Razorenov S.1,2, Krüger L.3
-
隶属关系:
- Institute of Problems of Chemical Physics
- Tomsk State University
- Freiberg University of Mining and Technology
- 期: 卷 63, 编号 3 (2018)
- 页面: 357-362
- 栏目: Solid State
- URL: https://journals.rcsi.science/1063-7842/article/view/200919
- DOI: https://doi.org/10.1134/S1063784218030210
- ID: 200919
如何引用文章
详细
Based on the registration and analysis of the full wave profiles, the Hugoniot elastic limit and spall strength of ceramics based on tungsten carbide with different cobalt content are measured. We also study the influence of the cobalt content on the mechanical characteristics of tungsten carbide such as hardness, fracture strength, Young’s modulus, shear modulus, and sound velocity. It is shown that in the process of spalling, the failure stresses grow and the dynamic elastic limit decreases almost linearly within the scatter of their values with growing cobalt content; moreover, the value of the Hugoniot elastic limit is abruptly practically halved as the cobalt content grows from 0 to 2 wt %.
作者简介
A. Savinykh
Institute of Problems of Chemical Physics; Tomsk State University
编辑信件的主要联系方式.
Email: savas@ficp.ac.ru
俄罗斯联邦, Chernogolovka, Moscow oblast, 142432; Tomsk, 634050
K. Mandel
Freiberg University of Mining and Technology
Email: savas@ficp.ac.ru
德国, Freiberg, 09599
S. Razorenov
Institute of Problems of Chemical Physics; Tomsk State University
Email: savas@ficp.ac.ru
俄罗斯联邦, Chernogolovka, Moscow oblast, 142432; Tomsk, 634050
L. Krüger
Freiberg University of Mining and Technology
Email: savas@ficp.ac.ru
德国, Freiberg, 09599