Ionic conductivity of binary fluorides of potassium and rare earth elements

Resumo

The ionic conductivity s of KYF₄ and K₂RF₅ single crystals (R = Gd, Ho, Er) and KNdF₄ and K₂RF₅ ceramic samples (R = Dy, Er) has been studied in the temperature range of 340–500°C. A comparative analysis of the σ values for these objects has been performed. Binary fluorides of potassium and rare earth elements were synthesized by the hydrothermal method (temperature 480°C, pressure 100–150 MPa) in the R₂O₃–KF–H₂O systems. The σ values of tetraf luorides are 3 × 10^–5 S/cm (KYF₄ single crystal) and 3 × 10^–6 S/cm (KNdF₄ ceramics) at 435°C. A K₂ErF₅ single crystal with σ = 1.2 × 10^–4 S/cm at 435°C has the maximum value of ionic conductivity among pentafluorides. The anisotropy of ionic transport was found in K₂HoF₅ single crystals, σ_∥c/σ_⊥c = 2.5, where σ_∥c and σ_⊥c are, respectively, the conductivities along the crystallographic c axis and in the perpendicular direction.