Investigating 64Zn+ ion-doped silicon under conditions of hot implantation

Аннотация

The results from visualizing the structure and identifying the composition of surface and the nearsurface layers of CZ n-Si (100) implanted by ⁶⁴Zn⁺ ions with dose of 5 × 10¹⁶ cm^–2 and energy of 50 keV under conditions of a substrate heated to 350°C are presented. It is found that there is no Si amorphization after Zn implantation, and only one layer 200 nm thick forms and is damaged because of radiation-induced defects. Zn nanoparticles 10–100 nm in size are found on a sample’s surface and in its near-surface layer. Computer analysis and mapping of the elemental and phase composition of FIB crater walls and the surface show that the main elements (54%) in the sample near-surface layer are Si, O, and Zn. The presence of ZnO phase is recorded to a depth of 20 nm in the sample.