Мақаланы E-mail арқылы жіберу Structural and Optical Properties of (110) Plane Textured SnO2:Zn Thin Films
- Авторлар: Bannur M.S.1, Maddani K.I.1, Mathad S.N.1, Patil P.S.1
-
Мекемелер:
- Department of Physics
- Шығарылым: Том 28, № 1 (2019)
- Беттер: 34-38
- Бөлім: Article
- URL: https://journals.rcsi.science/1061-3862/article/view/196021
- DOI: https://doi.org/10.3103/S1061386219010035
- ID: 196021
Дәйексөз келтіру
Ашық рұқсат
Рұқсат берілді
Тек жазылушылар үшін
Аннотация
SnO2:xZn thin films (x = 0, 1, 3, 5, 10, 15 wt%) were deposited onto a glass substrate by ultrasonic spray pyrolysis at 350°C and characterized by XRD, UV–VIS spectra, AFM imaging, and texture analysis. All deposited thin films exhibited preferential orientation along the (110) plane. The films were highly transparent (about 80%) in the visible. Upon an increase in x, the band gap energy of the films decreased from 3.7 eV to 3.3 eV.
Негізгі сөздер
Авторлар туралы
M. Bannur
Department of Physics
Хат алмасуға жауапты Автор.
Email: bannurmahesh@gmail.com
Үндістан, Haliyal, Karnataka, 581329
K. Maddani
Department of Physics
Хат алмасуға жауапты Автор.
Email: ki_maddani@rediffmail.com
Үндістан, Dharwad, Karnataka, 580002
S. Mathad
Department of Physics
Хат алмасуға жауапты Автор.
Email: physicssiddu@gmail.com
Үндістан, Hubballi, Karnataka, 589030
P. Patil
Department of Physics
Email: physicssiddu@gmail.com
Үндістан, Hubballi, Karnataka, 589030
Қосымша файлдар