Мақаланы E-mail арқылы жіберу Solution-Combustion Synthesis of LiNi1/3Co1/3Mn1/3O2 as a Cathode Material for Lithium-Ion Batteries
- Авторлар: Zhuravlev V.D.1, Pachuev A.V.2, Nefedova K.V.1, Ermakova L.V.1
-
Мекемелер:
- Institute of Solid State Chemistry, Ural Branch
- Public Corporation SATURN
- Шығарылым: Том 27, № 3 (2018)
- Беттер: 154-161
- Бөлім: Article
- URL: https://journals.rcsi.science/1061-3862/article/view/195973
- DOI: https://doi.org/10.3103/S1061386218030147
- ID: 195973
Дәйексөз келтіру
Ашық рұқсат
Рұқсат берілді
Тек жазылушылар үшін
Аннотация
A cathode material for lithium-ion batteries–LiNi1/3Co1/3Mn1/3O2–was prepared by solution combustion synthesis and characterized by XRD, SEM, and galvanostatic charge/discharge cycling. The sample calcined at 950°C for 10 h showed best charge/discharge performance. An initial discharge capacity (C) of 150.5 mA h g–1 retained 95.7% of its value after 75 charge/discharge cycles at Ic = 14 mA g–1 (0.2C rate), Id = 70 mA g–1 (0.5C rate).
Негізгі сөздер
Авторлар туралы
V. Zhuravlev
Institute of Solid State Chemistry, Ural Branch
Хат алмасуға жауапты Автор.
Email: zhvd@ihim.uran.ru
Ресей, Yekaterinburg, 620990
A. Pachuev
Public Corporation SATURN
Email: zhvd@ihim.uran.ru
Ресей, Krasnodar, 350072
K. Nefedova
Institute of Solid State Chemistry, Ural Branch
Email: zhvd@ihim.uran.ru
Ресей, Yekaterinburg, 620990
L. Ermakova
Institute of Solid State Chemistry, Ural Branch
Email: zhvd@ihim.uran.ru
Ресей, Yekaterinburg, 620990
Қосымша файлдар