Мақаланы E-mail арқылы жіберу Superconducting Nb3Al by combustion synthesis: Structural characterization
- Авторлар: Hafs A.1, Benaldjia A.2, Hafs T.2
-
Мекемелер:
- University of El Tarf
- University of Annaba
- Шығарылым: Том 25, № 3 (2016)
- Беттер: 159-165
- Бөлім: Article
- URL: https://journals.rcsi.science/1061-3862/article/view/195693
- DOI: https://doi.org/10.3103/S106138621603002X
- ID: 195693
Дәйексөз келтіру
Ашық рұқсат
Рұқсат берілді
Тек жазылушылар үшін
Аннотация
We report on the synthesis of superconducting Nb3Al intermetallic with a critical temperature of 18 K. Nb–3Al powder compacts were used to fabricate Nb3Al intermetallic by Mechanically Activated SHS (MA-SHS) and Mechanically Activated ElectroThermal Explosion (MA-ETE). Phase composition of the obtained samples was characterized by XRD, SEM, optical microscopy, EDX, and atomic emission spectroscopy (AES).
Негізгі сөздер
Авторлар туралы
A. Hafs
University of El Tarf
Хат алмасуға жауапты Автор.
Email: hafsali2006@yahoo.fr
Алжир, El Tarf, 36000
A. Benaldjia
University of Annaba
Email: hafsali2006@yahoo.fr
Алжир, Annaba, 23000
T. Hafs
University of Annaba
Email: hafsali2006@yahoo.fr
Алжир, Annaba, 23000
Қосымша файлдар