CaV0.5Mo0.5xxTixO3 – δ as a Promising Anode Material for Solid-Oxide Fuel Cells with LSGM Electrolyte


Дәйексөз келтіру

Толық мәтін

Ашық рұқсат Ашық рұқсат
Рұқсат жабық Рұқсат берілді
Рұқсат жабық Тек жазылушылар үшін

Аннотация

CaV0.5Mo0.5 – xTixO3 – δ samples with the perovskite structure were studied as a promising anode material for fuel cells with electrolyte based on substituted lanthanum gallate La0.88Sr0.12Ga0.82Mg0.18O2.85 (LSGM). According to X-ray diffraction data, the solid-solution homogeneity region lies from х = 0 to х = 0.25. It is shown that CaV0.5Mo0.25Ti0.25O3 – δ is compatible with the LSGM-based electrolytes as regards both its chemistry and the coefficient of thermal expansion. Substitution of titanium leads to a decrease in the total conductivity but extends the p(O2) range of phase stability of this material. It is demonstrated that in its composite with LSGM this material becomes more resistant to oxidation.

Авторлар туралы

S. Belyakov

Institute of High Temperature Electrochemistry, Ural Branch

Хат алмасуға жауапты Автор.
Email: bca2@mail.ru
Ресей, Yekaterinburg, 142432

S. Shkerin

Institute of High Temperature Electrochemistry, Ural Branch

Email: bca2@mail.ru
Ресей, Yekaterinburg, 142432

A. Kuz’min

Institute of High Temperature Electrochemistry, Ural Branch; Ural Federal University named after the First President of Russia B.N. Yeltzyn

Email: bca2@mail.ru
Ресей, Yekaterinburg, 142432; Yekaterinburg, 119992

Қосымша файлдар

Қосымша файлдар
Әрекет
1. JATS XML

© Pleiades Publishing, Ltd., 2017