Мақаланы E-mail арқылы жіберу Preparation of a Structural Polyimide Foam Plastic Based on a Bulk Copolymer of Acrylonitrile and Methacrylic Acid
- Авторлар: Safonov A.1,2, Kornienko P.1, Shirshin K.3,4
-
Мекемелер:
- Kargin Research Institute of Polymer Chemistry and Technology with Pilot Plant
- Lobachevsky State University
- Alekseev State Technical University
- Khoma Company
- Шығарылым: Том 96, № 4 (2023)
- Беттер: 397-402
- Бөлім: Articles
- URL: https://journals.rcsi.science/0044-4618/article/view/247300
- DOI: https://doi.org/10.31857/S0044461823040102
- EDN: https://elibrary.ru/OGACCT
- ID: 247300
Дәйексөз келтіру
Ашық рұқсат
Рұқсат берілді
Тек жазылушылар үшін
Аннотация
Foaming of particles of acrylonitrile–methacrylic acid copolymer in the temperature interval 160–220°С was studied. As shown by IR spectroscopy, the final polymer matrix of the foam plastics consists of glutarimide fragments. Thermogravimetric analysis shows that the products start to degrade at a high temperature (about 350°С). The effect of the prolonged heat treatment at 150–190°С on the physicomechanical characteristics of the foamed plastics was examined.
Негізгі сөздер
Авторлар туралы
A. Safonov
Kargin Research Institute of Polymer Chemistry and Technology with Pilot Plant; Lobachevsky State University
Email: acjournal.nauka.nw@yandex.ru
Dzerzhinsk, 606000, Nizhny Novgorod oblast, Russia; 603950, Nizhny Novgorod, Russia
P. Kornienko
Kargin Research Institute of Polymer Chemistry and Technology with Pilot Plant
Email: acjournal.nauka.nw@yandex.ru
Dzerzhinsk, 606000, Nizhny Novgorod oblast, Russia
K. Shirshin
Alekseev State Technical University; Khoma Company
Хат алмасуға жауапты Автор.
Email: acjournal.nauka.nw@yandex.ru
603950, Nizhny Novgorod, Russia; Dzerzhinsk, 606000, Nizhny Novgorod oblast, Russia
Әдебиет тізімі
- Kazantsev O. A, Shirshin K. V, Kornienko P. V., Sivokhin A. P. Achievements and prospects for the synthesis of poly(meth)acrylimide foams. Stage of the thermal imidisation of polymer precursors // Cellular Polymers. 2021. V. 40. N 1. Р. 31-52. https://doi.org/10.1177/0262489320934258
- Корниенко П. В., Ширшин К. В., Горелов Ю. П. Получение конструкционных пенополи-метакрилимидов на основе сшитых сополимеров акрилонитрила и метакриловой кислоты // ЖПХ. 2012. Т. 85. № 11. С. 1842-1846. https://www.elibrary.ru/acllis
- Корниенко П. В., Ширшин К. В., Горелов Ю. П. Получение и свойства вспененных материалов на основе сополимеров акрилонитрила и метакриловой кислоты // ЖПХ. 2013. Т. 86. № 1. С. 96-100. https://www.elibrary.ru/drmodb
- Pat. WO 052360 A1 (publ. 2019). Process for injection moulding polymer compounds comprising poly (meth) acrylimide foam particles.
- Pat. US 10207435 B2 (publ. 2019). Pressure-dependent foam moulding of poly(meth)acrylimide particles in closed moulds for producing rigid foam cores.
- Корниенко П. В., Ширшин К. В., Горелов Ю. П., Кузнецова А. В., Червякова Г. Н., Хохлова Т. А. Получение вспененных полиимидных материалов на основе акрилонитрила и (мет)акриловой кислоты // Пласт. массы. 2013. № 6. С. 14-18. https://www.elibrary.ru/rqrbfd
- Литосов Г. Э., Родин А. С., Дворко И. М., Панфилов Д. А., Лавров Н. А. Исследование влияния газообразователей на физико-механические характеристики композиций на основе полиакриламида // Клеи. Герметики. Технологии. 2022. № 4. С. 28-34. https://doi.org/10.31044/1813-7008-2022-0-4-28-34 https://www.elibrary.ru/kcrrkw
- Преч Э., Бюльманн Ф., Аффольтер К. Определение строения органических соединений / Пер. с англ. М.: Мир, 2006. 302 с.
- Наканиси К. Инфракрасные спектры и строение органических соединений / Пер. с англ. Под ред. А. А. Мальцева. М.: Мир, 1965. 215 с.