Phase Composition Formation in a V-1469 Alloy (Al–Cu–Li System) during Friction Stir Welding
- Авторы: Betsofen S.1, Sbitneva S.2, Panteleev M.2, Bakradze M.2, Gordeeva M.1, Knyazeva Y.1
-
Учреждения:
- National Research University Moscow Aviation Institute
- All-Russia Institute of Aviation Materials VIAM
- Выпуск: Том 2018, № 11 (2018)
- Страницы: 1059-1066
- Раздел: Article
- URL: https://journals.rcsi.science/0036-0295/article/view/172710
- DOI: https://doi.org/10.1134/S0036029518110046
- ID: 172710
Цитировать
Аннотация
The morphology of the intermetallic phases and their contents in the welded joint zones of a V‑1469 alloy (Al–Cu–Li system) are studied by X-ray diffraction and transmission electron microscopy. Welding is shown to change the phase composition, the crystallographic texture, and the microhardness of the alloy. According to quantitative X-ray diffraction analysis, the T1-phase content decreases and the δ'-phase content increases in the weld metal. As a result, the microhardness in the weld zone decreases, since the T1 phase is much stronger hardener than the δ' phase. This effect weakens when the weld root is approached.
Об авторах
S. Betsofen
National Research University Moscow Aviation Institute
Автор, ответственный за переписку.
Email: s.betsofen@gmail.com
Россия, Moscow, 125993
S. Sbitneva
All-Russia Institute of Aviation Materials VIAM
Email: s.betsofen@gmail.com
Россия, Moscow, 105005
M. Panteleev
All-Russia Institute of Aviation Materials VIAM
Email: s.betsofen@gmail.com
Россия, Moscow, 105005
M. Bakradze
All-Russia Institute of Aviation Materials VIAM
Email: s.betsofen@gmail.com
Россия, Moscow, 105005
M. Gordeeva
National Research University Moscow Aviation Institute
Email: s.betsofen@gmail.com
Россия, Moscow, 125993
Yu. Knyazeva
National Research University Moscow Aviation Institute
Email: s.betsofen@gmail.com
Россия, Moscow, 125993